Semiconductor device and method for fabricating the same

ABSTRACT

A semiconductor device is formed by depositing a nitride material having a lower etch rate than an oxide material over or between buried gates when forming a metal contact at an end portion of a cell region, to prevent a lower substrate from being etched during an etching process forming a metal contact hole. The semiconductor device includes at least one buried gate formed in a device isolation film of a semiconductor substrate, an etch stop film formed over and between the buried gates, and a metal contact formed perpendicular to the buried gate in the etch stop film.

CROSS-REFERENCE TO RELATED APPLICATION

The present application claims priority to Korean patent application No. 10-2012-0086458 filed on 7 Aug. 2012, which is incorporated by reference in its entirety.

BACKGROUND OF THE INVENTION

Embodiments of the present invention relate to a semiconductor device and a method for fabricating the same, and more particularly to a technology for depositing a nitride material having a lower etch rate than an oxide material over or between buried gates when forming a metal contact at an end portion of a cell region.

Although the demand of implementing high-capacity dynamic random access memory (DRAM) is rapidly increasing, there is difficulty in increasing chip size, resulting in a limitation in increasing storage capacity of DRAM. The larger the chip size, the less the number of chips on each wafer, resulting in a reduction of productivity. Therefore intensive research is being conducted into a variety of methods for reducing a cell region by varying a cell layout so as to form a large number of memory cells on one wafer.

A buried gate structure has been developed as an example of the above-mentioned methods. The buried gate is located below a semiconductor silicon substrate and a metal contact for voltage supply (or power supply) to the buried gate is required.

Usually, a metal contact transmits input/output (I/O) operation signals to the buried gate is formed in a larger size than that of underlying buried gate.

Thus, if misalignment occurs in a masking process for metal contact formation, a device isolation film between the buried gates (BGs) in a cell region is attacked. Furthermore, a semiconductor substrate (Sub) below the device isolation film also might be attacked. It causes current leakage or an electrical short, resulting in reduction of reliability of the semiconductor device.

In order to solve the above-mentioned problems, an over-etch process in the cell region should be refrained from so that the metal contact in the cell region is formed more shallow. For example, a bottom of the metal contact can be formed at a higher level than any surface of the substrates 101 a, 101 b, 101 c. However, a depth of the metal contact in the cell region cannot be arbitrarily adjustable because another metal contact is formed, in a simultaneous process, in a peripheral region so as to extend down to a substrate in the peripheral region.

BRIEF SUMMARY OF THE INVENTION

Various embodiments of the present invention are directed to providing a semiconductor device and a method for fabricating the same that substantially obviate one or more problems due to limitations and disadvantages of the related art, including those disclosed herein.

An embodiment of the present invention relates to a semiconductor device in which a nitride material having a low etch rate is deposited over or between buried gates when forming a metal contact at an end portion of a cell region to prevent a lower substrate from being etched when forming a metal contact hole over the buried gates, and a method for forming the semiconductor device.

In accordance with an aspect of the present invention, a semiconductor device includes at least one buried gate formed in a device isolation film of a semiconductor substrate; an etch stop film formed over and between the buried gates; and a metal contact formed in the etch stop film, perpendicular to the buried gate.

The etch stop film is formed of a material having a lower etch rate than the device isolation film. The etch stop film is formed of a nitride film.

The buried gate, the etch stop film, and the metal contact are formed in an end portion of a cell region.

In accordance with another aspect of the present invention, a method for fabricating a semiconductor device includes forming an insulation film in a cell region including a buried gate and a bit line structure and in a peripheral region including a peri-gate structure; forming an open region to expose a sidewall of the buried gate located in an end portion of the cell region, by etching some portions of the insulation film located in the end portion of the cell region; depositing an etch stop material over the cell region including the open region and over the peripheral region; forming an etch stop film by etching the etch stop material in the cell region using a cell-open mask; forming a first metal contact hole, perpendicular to the buried gate, in the etch stop film; and forming a metal contact by filling a conductive material in the first metal contact hole.

The step of forming the open region includes: simultaneously forming a first trench extending to a device isolation film in a center part of the cell region.

The step of depositing the etch stop material includes: depositing the etch stop material over the first trench.

The step of depositing the etch stop material includes: depositing the etch stop material over and between the buried gates.

The step of forming the etch stop film includes: forming a second trench for storage node formation by etching the etch stop material in a center part of the cell region; and depositing a conductive material in the second trench.

The step of forming the first metal contact hole perpendicular to each buried gate includes: simultaneously forming a second metal contact hole at both sides of the peri-gate structure in the peripheral region.

The etch stop film material has a lower etch rate than the device isolation film. The etch stop film material is a nitride material.

In accordance with another aspect of the present invention, a semiconductor device includes first power supply contacts provided in a cell end region; cell gates formed below the first power supply contacts and formed in a first device isolation film of the cell end region, respectively; and an etch stop film extending from between the first power supply contacts to between the cell gates.

The device further include a second power supply contact coupled to an active region in a peripheral region, wherein the etch stop film extends down to a first level, and wherein the second power supply contact extends down to a second level higher than the first level.

The first power supply contacts are coupled to the cell gates, respectively, and wherein the second power supply contact is coupled to the active region.

The etch stop film extends down to a first level, and wherein the cell gates extends down to a third level lower than the first level.

The first device isolation film extends down to a fourth level lower than the third level.

The etch stop film extends down to a first level, and wherein first power supply contacts extend down to a fifth level higher than the first level.

The fifth level is substantially the same as a top surface of any of the cell gates.

The etch stop film extends down to a first level, and wherein an upper surface of a substrate in the cell end region extends up to a sixth level higher than the first level.

The etch stop film has a first etch selectivity with respect to a given etching condition, wherein the first device isolation film has a second etch selectivity with to the given etching condition, and wherein the first etch selectivity is lower than the second etch selectivity.

The etch stop film includes an nitride-containing layer, and wherein the first device isolation film includes a oxide-containing layer.

The device further include an insulating layer provided in the peripheral region, defining the second power supply contact, and having a third etch selectivity, wherein the etch stop film has a first etch selectivity with respect to a given etching condition, and wherein the first etch selectivity is lower than the third etch selectivity with respect to the given etching condition.

The first device isolation film has a second etch selectivity with to the given etching condition, and wherein the third etch selectivity is substantially the same as the second etch selectivity.

The device further include a cell center region laterally extending from the cell end region, a storage node contact provided in the cell center region and extending down to an eighth level higher than the first level.

The cell gates extend to the cell center region, and wherein the storage node contact is coupled to any of the cell gates.

It is to be understood that both the foregoing general description and the following detailed description of the present invention are only exemplary and are intended to provide further explanation of the invention as claimed, but are not limited to the described embodiments.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross-sectional view illustrating a semiconductor device according to an embodiment of the present invention.

FIGS. 2A to 2G are cross-sectional views illustrating a method for forming a semiconductor device according to an embodiment of the present invention.

DESCRIPTION OF EMBODIMENTS

Reference will now be made in detail to embodiments of the present invention, examples of which are illustrated in the accompanying drawings. Wherever possible, the same reference numbers are used throughout the drawings to refer to the same or like portions. In the following description of the present invention, a detailed description of related known configurations or functions incorporated herein may be omitted for clarity of the subject matter of the present invention.

In accordance with the following description of the present invention, a material having a low etch rate is deposited over or between buried gates of the end portion of a cell region when forming a metal contact at the end portion of the cell region, so that a lower substrate is prevented from being etched during an etching process for metal contact formation. The above technical principles can be applied to all kinds of semiconductor devices including semiconductor elements.

A semiconductor device and a method for fabricating the same according to embodiments of the present invention will hereinafter be described with reference to FIGS. 1 to 2F.

FIG. 1 is a cross-sectional view illustrating a semiconductor device according to an embodiment of the present invention.

Referring to FIG. 1, the semiconductor device according to an embodiment of the present invention includes a cell-region center portion (i), a cell-region end portion (ii), and a peripheral region (iii).

The cell-region center portion (i) includes a bit line structure 110 formed over a semiconductor substrate 101 a including a device isolation film 103 a and a buried gate 105 a. In the cell-region center portion (i), an etch stop film 125 a is formed over the device isolation film 103 a. A storage node contact 129 is formed between the etch stop film 125 a and the bit line structure 110. The bit line structure 110 includes a poly layer 109, a tungsten layer 111, and a hard mask nitride film 113 a. The cell-region center portion (i) further includes a gate hard mask 107 a and interlayer insulation films 115 a, 131 a, as described further herein.

The cell-region end portion (ii) includes a device isolation film 103 b and a buried gate 105 b in a semiconductor substrate 101 b. In the cell-region end portion (ii), an etch stop film 125 b is formed at an upper portion and sidewalls of the buried gate 105 b, and a metal contact hole 133 a is formed perpendicular to an upper portion of the buried gate 105 b. The cell-region end portion (ii) further includes a gate hard mask 107 b and interlayer insulation films 115 b, 131 b, as described further herein. The gate hard mask 107 a, 107 b include a nitride film. Hereinafter, the buried gate 105 b and the gate hard mask 107 b are collectively referred to as a cell gate structure.

The peripheral region (iii) includes a peri-gate structure 122 formed over a semiconductor substrate 101 c including a device isolation film 103 c, and a metal contact hole 133 b is formed at both sides of the peri-gate structure 122. The peri-gate structure 122 includes a gate oxide film 117, a polysilicon layer 119, a tungsten layer 121, and a hard mask nitride film 113 b. The peripheral region (iii) further includes interlayer insulation films 115 c, 131 c, as described further herein.

As described above, the etch stop film 125 b is deposited over the buried gates 105 b of the cell-region end portion (ii) including the metal contact hole 133 a, and also between the buried gates 105 b, to prevent the metal contact hole 133 a from extending to the device isolation film 103 b and the semiconductor substrate 101 b.

The etch stop film 125 b extends down to a level which is lower than a upper surface of the substrate 101 b, preferably lower than a top surface of the buried gate 105 b.

FIGS. 2A to 2F are cross-sectional views illustrating a method for forming a semiconductor device according to an embodiment of the present invention. The method for forming the semiconductor device according to the embodiment of the present invention will hereinafter be described with reference to FIGS. 2A to 2F.

Referring to the cell-region center portion (i) shown in FIG. 2A, a semiconductor substrate 101 a including a device isolation film 103 a is formed using a hard mask pattern (not shown) as a mask so that a first trench (not shown) is formed. In the cell-region end portion (ii), a second trench (not shown) is formed in the device isolation film 103 b which is formed in the semiconductor substrate 101 b.

Thereafter, a gate insulation film (not shown) and a conductive material are deposited in the first and the second trenches in the cell-region center portion (i) and in the cell-region end portion (ii), so that a buried gate 105 a and a buried gate 105 b are formed in the cell-region center portion (i) and the cell-region end portion (ii), respectively. In an embodiment, the conductive material may include titanium (Ti) and tungsten (W), and may have a sufficient thickness in a manner that the trench can be sufficiently filled with the conductive material.

Thereafter, gate hard masks 107 a and 107 b are formed over the buried gates 105 a and 105 b, respectively, and interlayer insulation films 115 a, 115 b are formed over the entire surface of an upper portion of the semiconductor substrate including the gate hard masks 107 a, 107 b in the cell-region center portion (i) and in the cell-region end portion (ii), respectively. A bit line structure 110 is formed at one side of an upper portion of an active region of the cell-region center portion (i). The bit line structure 110 may be formed by sequential deposition of a poly layer 109, a tungsten (W) layer 111, and a hard mask nitride film 113 a. An interlayer insulation film 115 a is formed over the entire surface of the bit line structure 110, and over the semiconductor substrate 101 a.

In the peripheral region (iii), a gate oxide film 117 and a peri-gate structure 122 are formed over a semiconductor substrate 101 c including a device isolation film 103 c, and an interlayer insulation film 115 c is formed over the entire surface of a lateral side of the peri-gate structure 122. Here, the peri-gate structure 122 is formed by sequential deposition of a gate oxide film 117, a polysilicon layer 119, a tungsten (W) layer 121 and a hard mask nitride film 113 b.

In an embodiment, the interlayer insulation film (115 a, 115 b, 115 c) may be formed of an oxide-based material.

Thereafter, as shown in FIG. 2B, a mask (not shown) for open region formation is formed, and open regions (123 a, 123 b) are formed over the device isolation films (103 a, 103 b) of the cell-region center and end portions (i, ii) using the formed mask (not shown). In the cell-region center portion (i), the open region 123 a exposes the buried gate 105 a formed in the device isolation film 103 a. In the cell-region end portion (ii), the open region 123 b is etched, preferably until a sidewall of the buried gate 105 b is exposed.

Referring to FIG. 2C, etch stop layers (125 a, 125 b, 125 c) are deposited over the entire surface of the open regions (123 a, 123 b) of the cell-region center portion (i) and the cell-region end portion (ii) shown in FIG. 2B, and also over the interlayer insulation film 115 c and the hard mask nitride film 113 b of the peripheral region (iii). The etch stop layer 125 b extends between gate hard mask 107 b formed in the cell-region end portion (ii). The etch stop layer 125 b may further extend between the buried gates 105 b in the cell-region end portion (ii).

In an embodiment, the etch stop film (125 a, 125 b or 125 c) may be formed of a material having a lower etch rate than the interlayer insulation film (115 a, 115 b or 115 c). For example, if the interlayer insulation film (115 a, 115 b or 115 c) is formed of an oxide material, the etch stop film (25 a, 125 b or 125 c) may be formed of a nitride film having a lower etch rate than an oxide material.

More specifically, the etch stop film 125 b has an etch rate lower than the device isolation film 103 b in the cell region end portion (ii).

Referring to FIG. 2D, a cell-open mask (not shown) for forming a storage node contact is formed in the cell-region center portion (i). The interlayer insulation film (115 a) and the etch stop film (125 a) over the interlayer insulation films (115 a) are etched using the cell-open mask (not shown). As a result, a storage node contact hole 127 is formed at both sides of the bit line structure 110 in an active region of the cell-region center portion (i). The etch stop film 125 b in the cell-region end portion (ii) is subject to planarization. In an embodiment, the etch stop films (125 a, 125 b) and the interlayer insulation film (115 a) may be wet-etched.

Referring to FIG. 2E, a conductive material fills the storage node contact hole 127 in the cell-region center portion (i), and the resultant conductive material is then planarized, so that the etch stop film 125 a is exposed. Thereby, a storage node contact 129 is formed. In an embodiment, the conductive material may be formed of a poly material, and the planarization may be carried out through Chemical Mechanical Polishing (CMP) or etching. The etch stop film 125 b formed over the peripheral region (iii) is planarized to a predetermined thickness so that an upper portion of the interlayer insulation film 115 c is exposed.

Referring to FIG. 2F, interlayer insulation films (131 a, 131 b, 131 c) are deposited over the entire upper surfaces of the cell-region center portion (i), the cell-region end portion (ii), and the peripheral region (iii). The metal contact holes (133 a, 133 b) are then formed in the cell-region end portion (ii) and the peripheral region (iii), respectively.

The metal contact hole 133 a of the cell-region end portion (ii) is vertically formed over the buried gate 105 b by etching the etch stop film 125 b. The etch stop film 125 b having a predetermined thickness remains both of sides the buried gate 105 b. In addition, a metal contact hole 133 b is formed in the peripheral region (iii) such that the active region of the semiconductor substrate 101 c of both sides of the peri-gate structure 122 is exposed.

In an embodiment, the metal contact hole 133 a exposes the buried gate 105 b. The metal contact hole 133 b exposes the substrate 101 c in the peripheral region (iii).

Thereafter, Referring to FIG. 2G, metal material fills the metal contact holes (133 a, 133 b) to form first and second metal contacts (or a first and second power supply contacts) 143 a, 143 b. Power (or voltage) is supplied from outside to the cell gate structure 105 b, 107 b and the peri-gate structure 122 through the first metal contact (the first power supply contact) 143 a and the second metal contact (the second power supply contact) 143 b, respectively.

The metal contact hole 133 a in the cell-region end portion (ii) extends down to the top surface of the buried gate 105 b or deeper. The metal contact hole 133 b in the peripheral region (iii) extends to a level which is substantially equal to or lower than a surface of the substrate 101 c.

Put another way, the metal contact hole 133 a in the cell-region end portion (ii) extends to the first level lower than the fourth level to which the metal contact hole 133 b in the peripheral region (iii) extends.

As described above, according to the embodiments of the present invention, the etch stop film 125 b is deposited over and between the buried gates 105 b of the cell-region end portion (ii). As a result, although misalignment occurs in the process for forming the metal contact hole 133 a, the etch stop film 125 b can prevent the semiconductor substrate from being etched.

In more detail, first, the etch stop film 125 b in the cell-region end portion (ii) extends down to the top surface of the buried gate 105 b or deeper. Second, the etch stop film 125 b has an etch selectivity lower than that of the device isolation film 103 b (c). Thus, under a given etching condition, the substrate 101 b in the cell-region end portion (ii) can be protected from being attacked during the process of forming the metal contact hole 133 a in the cell-region end portion (ii).

As is apparent from the above description, a nitride material having a lower etch rate than an oxide material is deposited over and between the buried gates, so that it can prevent the etching range for metal contact hole formation from extending to each buried gate or an oxide material located at a lateral surface of the buried gate, and therefore the semiconductor substrate is prevented from being exposed.

Those skilled in the art will appreciate that the present invention may be carried out in other specific ways than those set forth herein without departing from the spirit and essential characteristics of the present invention. The above exemplary embodiments are therefore to be construed in all aspects as illustrative and not restrictive. The scope of the invention should be determined by the appended claims and their legal equivalents, not by the above description, and all changes coming within the meaning and equivalency range of the appended claims are intended to be embraced therein. Also, it is obvious to those skilled in the art that claims that are not explicitly cited in each other in the appended claims may be presented in combination as an exemplary embodiment of the present invention or included as a new claim by a subsequent amendment after the application is filed.

The above embodiments of the present invention are illustrative and not limitative. Various alternatives and equivalents are possible. The invention is not limited by the type of deposition, etching polishing, and patterning steps described herein. Nor is the invention limited to any specific type of semiconductor device. For example, the present invention may be implemented in a dynamic random access memory (DRAM) device or non volatile memory device. Other additions, subtractions, or modifications are obvious in view of the present disclosure and are intended to fall within the scope of the appended claims. 

1-4. (canceled)
 5. A method for fabricating a semiconductor device comprising: forming an insulation film in a cell region including a buried gate and a bit line structure and in a peripheral region including a peri-gate structure; forming an open region to expose a sidewall of the buried gate located in an end portion of the cell region, by etching some portions of the insulation film located in the end portion of the cell region; depositing an etch stop material over the cell region including the open region and over the peripheral region; forming an etch stop film by etching the etch stop material in the cell region using a cell-open mask; forming a first metal contact hole, perpendicular to the buried gate, in the etch stop film; and forming a metal contact by filling a conductive material in the first metal contact hole.
 6. The method according to claim 5, wherein the step of forming the open region includes: simultaneously forming a first trench extending to a device isolation film in a center part of the cell region.
 7. The method according to claim 6, wherein the step of depositing the etch stop material includes: depositing the etch stop material over the first trench.
 8. The method according to claim 5, wherein the step of depositing the etch stop material includes: depositing the etch stop material over and between the buried gates.
 9. The method according to claim 5, wherein the step of forming the etch stop film includes: forming a second trench for storage node formation by etching the etch stop material in a center part of the cell region; and depositing a conductive material in the second trench.
 10. The method according to claim 5, wherein the step of forming the first metal contact hole perpendicular to each buried gate includes: simultaneously forming a second metal contact hole at both sides of the peri-gate structure in the peripheral region.
 11. The method according to claim 6, wherein the etch stop film material has a lower etch rate than the device isolation film.
 12. The method according to claim 5, wherein the etch stop film material is a nitride material. 13-26. (canceled) 